Dupa plasarea solicitării de comandă, in sectiunea Istoric puteti vedea cate solicitări de comandă mai avem de procesat inaintea dumneavoastra
Program de lucru: Luni - Vineri 9:00 - 18:00, pauza 13:00 - 14:00.
Se efectueaza lucrari de mentenanta la site si pot aparea erori. In cazul in care intampinati erori va rugam sa reincercati mai tarziu.
Ridicarea personala este disponibila pentru comenzile achitate in avans. Se pot ridica dupa ce sunt pregatite.
WOOW !!! Livrare gratuita la locker Easybox pentru comenzi mai mari de 98 RON !
No products
View larger
FormFutura ReForm rPET Filament - Off-Black, 2.85 mm, 50 g
8718924478677
New product
ReForm is a sustainable initiative within Formfutura to efficiently manage residual extrusion waste streams and re-use them into high-end upcycled filaments.
See Description for more details about the product.
Don't delay, buy today. Add to cart now!
This product is no longer in stock
- Write a review
- Remove this product from my favorite's list.
- Add this product to my list of favorites.
More info
Description
The ideology behind ReForm is to make 3D printing more sustainable - without having to make compromises on material properties - and yet keep it affordable. ReForm rPET is based on exactly the same unique formulation as our HDglass filament range but is made out of residual extrusion waste streams which are re-compounded and homogenized into a high-end and easy to print upcycled PETG-based filament with significantly less environmental impact.
Unique features
- 100% upcycled/recycled filament with retaining the unsurpassed printing properties of HDglass
- Less environmental impact by quality controlling and re-using extrusion waste streams
- Only residual waste streams of HDglass is being re-used, thus pure quality!
- Sustainable packaging
- ReForm filaments are spooled on easy to recycle and dispose of recycled cardboard spools
- ReForm filament is packaged in recycled carton boxes
- Compatible for printing at high speed
- Easy to print
- Nearly warp-free and perfect inter-layer adhesion
- Good first layer adhesion to a heated glass print bed and many other surfaces
General printing guidelines *
| Nozzle size: ≥ 0.15mm | Layer height: ≥ 0.1mm | Flow rate: ± 110 |
| Print temp: ± 200 - 240oC | Print speed: High | Retraction: Yes ± 6mm |
| Heat bed: ± 65 - 75oC | Fan speed: 0-30% | Experience level: Beginner |
*) Above displayed settings are meant as guidance to find your optimal print settings. These ranges in settings should work for most printers, but please do feel free to experiment outside these ranges if you think it is suitable for your printer. There is a lot of different type of printers, hot-ends, and printer offset that it is extremely difficult to give an overall one-size-fits-all setting.
Filament length
| p: 1.27 g/cc | 50 gr coil | 0.5 Kg spool |
| Ø 1.75mm | ± 16.4m | ± 327m |
| Ø 2.85mm | ± 6.2m | ± 123m |
| Properties | Typical value | Test Method | Test condition |
|---|---|---|---|
| Physical | |||
| Specific gravity | 1.27 g/cc | ASTM D792 | - |
| Melt flow rate | - | - | - |
| Water absorption | - | - | - |
| Moisture absorption | 0.13% | ASTM D570 | - |
| Mechanical | |||
| Impact strength | 7.2 KJ/m2 | ASTM D256 | Izod Notched @23oC (73oF) |
| Tensile strength | 50 Mpa | ASTM D638 | @Yield 50mm/min (2 inch/min) |
| Tensile modulus | 1940 Mpa | ISO 527 | 1mm/min |
| Elongation at break | 120% | ASTM D638 | 50mm/min (2 inch/min) |
| Flexural strength | 70.6 Mpa | ASTM D790 | 1.27mm/min (0.05 inch/min) |
| Flexural modulus | 2147.6 Mpa | ASTM D790 | 1.27mm/min (0.05 inch/min) |
| Hardness | 105 | ASTM D785 | Rockwell R-scale |
| Thermal | |||
| Print temperature | ± 195 - 225oC | - | - |
| Melting temperature | - | - | - |
| Viscat softening temp. | ± 70oC | ASTM D648 | @ 0.455 Mpa (66psi) |
| Optical | |||
| Haze | <1.0% | ASTM D1003 | - |
| Transmittance | 90% | ASTM D1003 | - |
| Gloss | - | - | - |