PLA Sakata 3D TEXTURE Wood Maple Filament 1.75 mm 450 g

View larger

Imaginile sunt utilizate exclusiv cu titlu de prezentare. Fotografiile nu creează obligații contractuale.

PLA Sakata 3D TEXTURE Wood Maple Filament 1.75 mm 450 g

Reference: 0104110000075109

Condition: New product

The texturized natural fibers based PLA, easy to print and with an astonishing finish and with a pleasant smell of wood.

See description for more details about the product.

Add to cart now!

More details

This product is no longer in stock

Notify me when available

Write a review

Remove this product from my favorite's list.

Add this product to my list of favorites.

More info

Description

SAKATA 3D PLA Texture Maple Wood filament is suitable for all consumer-grade 3D FDM/FFF printers. This filament is made from a biodegradable compound of PLA and natural wood fibers, specifically engineered for 3D printing applications. The biobased carbon content is > 75 %. It gives to 3D printed parts a realistic wooden look and feel. Made in Spain by POLIMERSIA GLOBAL S.L.

Filament Specifications	Value	Unit
Diameter	1.75 ± 0.05	mm
Max. roundness deviation	0.05	mm
Net weight	500	g

Physical Properties	Standard	Value	Unit
Melting temperature	ISO 3146-C	155	^oC

Mechanical Properties	Standard	Value	Unit
Tensile strength	ISO 527	47	MPa
Tensile modulus	ISO 527	2,900	MPa
Tensile elongation at break	ISO 527	6.5	%
Flexural strain at break	ISO 178	No break	%
Flexural strain at 3.5 % strain	ISO 178	64	MPa
Flexural modulus	ISO 178	2,950	MPa
Notched Charpy impact	ISO 179-1/1 eA	4.4	kJ/m²
Charpy impact	ISO 179-1/1 eU	21	kJ/m²

Print Setting	Value	Unit
Nozzle temp.	200-255 ^(*)	^oC
Bed temp.	Not needed (50-70 optional)	^oC
Bed modification	-	--
Fan speed	100	%
Layer height	0.1-0.3	mm
Shell thickness	0.8	mm
Print speed	Up to 90	mm/s