FormFutura StoneFil - Concrete, 1.75 mm, 500 g

View larger

Imaginile sunt utilizate exclusiv cu titlu de prezentare. Fotografiile nu creează obligații contractuale.

FormFutura StoneFil Filament - Concrete, 1.75 mm, 500 g

Reference: 8718924478370

Condition: New product

StoneFil is a PLA-based filament that is based on our modified and easy-to-print EasyFil PLA compound and is gravimetrically filled with 50% of powdered stone.

See Description for more details about the product.

Don't delay, buy today. Add to cart now!

More details

1 Item Items

Warning: Last items in stock!

Write a review

Remove this product from my favorite's list.

Add this product to my list of favorites.

More info

Description

This high "stone filling" has resulted in a 3D printer filament with remarkable aesthetic features and a significant higher material density up to 37% higher than “normal” PLA. StoneFil is an easy-to-print 3D printer filament and printed objects have an extremely matte stone-like finish with unique natural gradient color linings resulting in an exceptional chromatic spectrum per print. Every StoneFil printed object will have its own identity and unique gradient color shading.

Unique features

Easy to print
50% gravimetric powdered stone filling
- ±37% heavier than “normal” PLA
Matte and rough stone-like finish
Unique natural/organic gradient color linings
- Every print has its unique natural stone gradient color shading

General printing guidelines *

Nozzle size: ≥ 0.4mm	Layer height: ≥ 0.15mm	Flow rate: ± 110%
Print temp: ± 215 - 240^oC	Print speed: High / Medium	Retraction: Yes ± 5mm
Heat bed: ± 0 - 60^oC	Fan speed: 50-100%	Experience level: Beginner

*) Above displayed settings are meant as guidance to find your optimal print settings. These ranges in settings should work for most printers, but please do feel free to experiment outside these ranges if you think it is suitable for your printer. There is a lot of different type of printers, hot-ends, and printer offset that it is extremely difficult to give an overall one-size-fits-all setting.

Abrasiveness

StoneFil has a very high filling with stone powders and therefore the filament can have a slightly more abrasive effect on brass nozzles than unfilled filaments.

Filament length

p: 1.70 g/cc	50 gr coil	0.5 Kg spool
Ø 1.75mm	± 12.2m	± 122m
Ø 2.85mm	± 4.6m	± 46m

Nozzle cleaning

When printing with filled/composite filaments it is recommended to clean your nozzle immediately after printing by feeding 15-20cm PLA filament through your nozzle. This will make sure that any potential fillers are flown out of your nozzle. It is even better to use glow in the dark PLA as the extremely hard phosphorous particles are much more likely to scrape out residual waste from your nozzle.

Properties	Typical value	Test Method	Test condition
Physical
Specific gravity	1.7 g/cc	ISO 1183	-
Melt flow rate	94 g/10min	ISO 1133	210^oC/2.16Kg
Water absorption	-	-	-
Moisture absorption	-	-	-
Mechanical
Impact strength	2.9 KJ/m²	ISO 179	Charpy Notched @23^oC (73^oF)
Tensile strength	38.0 Mpa	ISO 527	@Yield 50mm/min (2 inch/min)
Tensile modulus	4760 Mpa	ISO 527	-
Elongation at break	33%	ISO 527	@ Break 50mm/min (2 inch/min)
Flexural strength	-	-	-
Flexural modulus	-	-	-
Hardness	-	-	-
Thermal
Print temperature	± 190 - 240^oC	-	-
Melting temperature	± 77 - 153^oC	ISO 11357	-
Viscat softening temp.	± 57^oC	ISO 306	VST/A/50 (50^oC/h, 10N)
Optical
Haze	-	-	-
Transmittance	-	-	-
Gloss	-	-	-